- LAMINATED COPPER CU DHP 99,9 CW024A SOFT ANNEALED
Technical Specifications In accordance with the standard EN 1652/1172 Density g/cm³ 8,92 Composition (approximate) % Cu≥99,9 – P 0,015÷0,040 Physical state R220 – H40 Mechanical Properties Tensile strength (approximate) N/mm² 220÷260 Yield strength N/mm² 140 min Elongation at rupture A% for thickness <2.5 mm ≥33 Elongation at rupture A% for thickness >2.5 mm ≥42 Hardness HV 40÷65 Dimensions and packaging COILS Width and formats (mm) 1000 Thicknesses (mm) 0,30 – 0,50 – 0,60 – 0,70 – 0,80 – 1,00 – 1,20 – 1,50 – 2,00 Standard packaging ø 300 – 400 or 508 STRAPS Width and formats (mm) starting from 8 Thicknesses (mm) 0,50 – 0,60 – 0,70 – 0,80 – 1,00 – 1,20 – 1,50 – 2,00 Standard packaging ø 300 – 400 or 508 Weight coils: 500 or 1000 kg – minicoils: 100 kg each SHEETS Width and formats (mm) 1000×2000 Thicknesses (mm) 0,30 – 0,50 – 0,60 – 0,70 – 0,80 – 1,00
– 1,20 – 1,50 – 2,00Standard packaging – Other sizes, alloys, finishes and thickness on request.
- CU DHP 99,9 CW024A HALF HARD
Technical Specifications In accordance with the standard EN 1652/1172 Density g/cm³ 8,92 Composition (approximate) % Cu≥99,9 – P 0,015÷0,040 Physical state R240 – H65 Mechanical Properties Tensile strength (approximate) N/mm² 240÷300 Yield strength N/mm² 180 min Elongation at rupture A% for thickness <2.5 mm ≥8 Elongation at rupture A% for thickness >2.5 mm ≥15 Hardness HV 65÷95 Dimensions and packaging COILS Width and formats (mm) 1000 – 1250 Thicknesses (mm) 0,45 – 0,50 – 0,55 – 0,60 – 0,70
– 0,80 – 1,00 – 1,20 – 1,50 – 2,00 – 2,50 – 3,00 – 4,00Standard packaging ø 300 – 400 or 508 STRAPS Width and formats (mm) starting from 8 Thicknesses (mm) 0,45 – 0,50 – 0,55 – 0,60 – 0,70 – 0,80 – 1,00 – 1,20 – 1,50 – 2,00 – 2,50 – 3,00 – 4,00 1.00 – 1.20 – 1.50 – 2.00 – 3.00 – 4.00 Standard packaging ø 300 – 400 or 508 Packaging on request coils int. ø 508 mm or 6 mini-coils Weight coils: 500 o 1000 kg – minicoils: 100 kg each SHEETS Width and formats (mm) 1000×2000 – 1250×2500 Thicknesses (mm) 0,45 – 0,50 – 0,55 – 0,60 – 0,65 – 0,70 – 0,80 – 0,90 – 1,00 – 1,20 – 1,50 – 2,00 – 2,50 – 3,00 – 4,00 – 5,00 Standard packaging – Other sizes, alloys, finishes and thickness on request.
- DRAWN HALF HARD ETP 99,9 CW004A
Technical Specifications In accordance with the standard EN 13601 – CW008A Density g/cm³ 8,92 Composition (approximate) % Cu≥99,900 – Pb≤0,005 – Bi≤0,0005 Mechanical Properties Tensile strength (approximate) N/mm² 260÷300 Yield strength N/mm² – Elongation at rupture A% for thickness <2.5 mm 8 Elongation at rupture A% for thickness >2.5 mm 15 Hardness HV – Dimensions and packaging STRAIGHT LENGTHS Width and formats (mm) 20 – 25 – 30 – 40 – 50 – 60 Thicknesses (mm) 2,00 – 3,00 – 4,00 – 5,00 Standard length (m) 4 Inner diameter (mm) – WIRE Width and formats (mm) 28 – 30 Thicknesses (mm) 1,50 – 2,00 – 2,50 – 3,00 – 4,00 Standard length (m) – Inner diameter (mm) 500 Other sizes, alloys, finishes and thickness on request.
- TECU®OXID LAMINATED COPPER
Technical Specifications In accordance with the standard EN 1172 – CW024A/CU DHP Density g/cm³ 8,92 Composition (approximate) % Cu >99,9 – P 0,015÷0,040 Mechanical Properties Tensile strength (approximate) N/mm² 240÷285 Extension N/mm² 180 – 230 Elongation at rupture A50 % ≥15 HV hardness max 90 Material not available in the warehouse but on request, thickness and formats to be verified.
- TECU®PATINA LAMINATED COPPER
Technical Specifications In accordance with the standard EN 1172 – CW024A/CU DHP Density g/cm³ 8,92 Composition (approximate) % Cu >99,9 – P 0,015÷0,040 Mechanical Properties Tensile strength (approximate) N/mm² 240÷285 Extension N/mm² 180 – 230 Elongation at rupture A50 % ≥15 HV hardness max 90 Material not available in the warehouse but on request, thickness and formats to be verified.
- TECU®ZINN LAMINATED COPPER
Technical Specifications In accordance with the standard EN 1172 – CW024A/CU DHP Density g/cm³ 8,92 Composition (approximate) % Cu >99,9 – P 0,015÷0,040 Mechanical Properties Tensile strength (approximate) N/mm² 240÷285 Extension N/mm² 180 – 230 Elongation at rupture A50 % ≥15 HV hardness max 90 Material not available in the warehouse but on request, thickness and formats to be verified.